Hot Press Boron Nitride Ceramic Rod

Hexagonal Boron Nitride has a microstructure similar to that of Graphite. In both materials this structure, made up of layers of tiny platelets, is responsible for excellent machinability and low-friction properties. we called hexagonal boron nitride (HBN) or white graphite. Boron nitride can be long-term used at 1800 degrees under vacuum atmosphere. With gas protection, Boron Nitride can be used at 2100°. Boron Nitride is with high thermal shock resistance, no cracks under extreme cold & high temperature. If you take out Boron Nitride from 1000 degree furnace and colding it within short minutes. It still won't break even repeat this test with 100 times. Material Properties： * High thermal conductivity * Excellent thermal shock resistance * Low thermal expansion * Exceptional heat resistance * Good Chemical Inertness * High electrical resistance * Low dielectric constant and loss tangent * High volume resistivity * Excellent machinability

Electric 12V 13V Alumina Ceramic Heating Element Heater Rod for Oxygen Sensor Advantages Ceramic Heater for Oxygen senster is used for heating oxygen sensors that detect the exhaust gas of vehicles and is equipped to most of automobile gasoline engines. Because the temperature can be rapidly raised, it is possible to activate the sensor immediately after the engine start which provides useful feedback to reduce emissions. 1.Based material: a.white alumina ceramic b.the content of alumina is no less than 95%. c.the tungsten slurry is printed on the ceramic tape, laminated by hot pressing, and thensintered under the protection of a hydrogen atmosphere at 1650 ° C 2.Ni-wires:N6 Ni-wires with 0.6mm diameter 3.Brazing material: siliver-copper braging alloy

Ceramic Heater for Soldering iron & Station: Alumina Ceramic Heaters are produced by implementing unique metallization and ceramic lamination processes. Due to the advanced manufacturing techniques utilized in the electric element, Alumina Heaters can provide higher reliability than ever before.Currently, applications include use as innovative types of heaters in the automotive, medical and semiconductor industries. a.Based material: white alumina ceramic, and the content of alumina is no less than 95%.The tungsten slurry is printed on the ceramic tape, laminated by hot pressing, and thensintered under the protection of a hydrogen atmosphere at 1650 ° C b.Ni-wires:N6 Ni-wires with 0.6mm diameter c.Brazing material: siliver-copper braging alloy Application: We are producing High Quality 24V 110V 220V Heating Element for Soldering Station with the advantages of energy-efficient,long lifetime,high insulation,super fast heatin up and eco-friendly.

Ceramic Pellet Igniter Information Ceramic Boiler Ignition Igniter surface can reach a permanent working temperature above 900℃;Since air can through and around inside and outside of the heater tube. Heat can be transferred from both inside and outside of ther heater element. Igniting wood chips, firewood, coal bricks or other biomass fuel. Specification: Voltage: 120V / 230V Power: 150W / 170W / 200W / 230W Tube Size: OD10.5 × ID6.5 × L78 mm Supporting Socket: NO.7 Lead wire: 300mm / 400mm / 500mm / 900mm (Customized is accept) Range of temperature: 800~1100 °C Alumina Pellet Igniter Advantages 1) Higher temperature, about twice of traditional metal sheathed heater; 2) Shorter ignition time, about 60~90 seconds 3) Electrically insulated with no exposed electric contacts 4) Wear and corrosion resistance 5) Long life time 6) Easy to install and replace 7) Long-lasting (non-aging). Tested to 100,000 cycles. 8) 800~1100°C at steady-state temperature.