Styrene-acrylic dispersion Novopol 001A

Aqueous dispersion of a copolymer of acrylic and methacrylic acid esters

Description

TECHNICAL SPECIFICATIONS Dispersion: Appearance White liquid Content of non-volatile substances, wt. % 50±1 Density, g/cm3 ~1.04 pH 7-9 Minimum Film Formation Temperature (MFFT), ºC ~0 Brookfield viscosity at 23°С, RVT/2/20, mPa×s 300-800 Conditional viscosity according to B3-4, from 15-30 Particle size, mcm 0.1-0.2 Resistance to mechanical agitation (5 min at 14000 rpm) Resistant The content of residual monomers, wt.% <0.1<br /> Film Appearance Transparent, elastic, slightly sticky Film tear strength, N/mm² ~3 Relative film elongation at break, % ~850 Water absorption (after 24 hours at 23°C and film thickness 0.27-0.32 mm), % 10-13 STORAGE The dispersion is recommended to be stored at a temperature of +2 to +35°C. . Warranty period of storage - 6 months Avoid freezing